Autor segons l'article: Fabregat-Sanjuan A; Ferrando F; De la Flor S
Departament: Enginyeria Mecànica
Autor/s de la URV: De la Flor Lopez, Silvia / Fabregat Sanjuan, Albert / Ferrando Piera, Francesc
Paraules clau: Ti Shape memory alloys Phase Niticu Internal friction Heat treatment Cu alloys
Resum: © 2015 The Authors. Internal friction (IF) and storage modulus evolution during the martensitic transformation were measured using the DMA technique in order to compare the effect of heat treatment on the behavior of IF in Ti44.6Ni5Cu (%at.) shape memory alloy. Two kinds of experiment were performed: IF measurements as a function of temperature and IF measurements at a fixed temperature to obtain the static term of the intrinsic internal friction. The results are compared with those obtained from DSC measurements. IF results show a clear dependence on the temperature of the heat treatment with distinctive regions that could be attributed to microstructural changes.
Àrees temàtiques: Química Materials science (miscellaneous) Materials science (all) Materiais General materials science Engenharias ii Biotecnología
Accès a la llicència d'ús: https://creativecommons.org/licenses/by/3.0/es/
Adreça de correu electrònic de l'autor: f.ferrando@urv.cat a.fabregat@urv.cat silvia.delaflor@urv.cat
Identificador de l'autor: 0000-0003-4450-2734 0000-0002-2878-1369 0000-0002-6851-1371
Data d'alta del registre: 2024-10-19
Versió de l'article dipositat: info:eu-repo/semantics/publishedVersion
Enllaç font original: https://www.sciencedirect.com/science/article/pii/S2214785315006379
URL Document de llicència: https://repositori.urv.cat/ca/proteccio-de-dades/
Referència a l'article segons font original: Materials Today: Proceedings. 2 S755-S758
Referència de l'ítem segons les normes APA: Fabregat-Sanjuan A; Ferrando F; De la Flor S (2015). Influence of Heat Treatment on Internal Friction Spectrum in NiTiCu Shape Memory Alloy. Amsterdam: Elsevier
DOI de l'article: 10.1016/j.matpr.2015.07.392
Entitat: Universitat Rovira i Virgili
Any de publicació de la revista: 2015
Tipus de publicació: Proceedings Paper