Biomimetic polymeric membrane for proton transport channeled by self-columnar assembly and sandwiched with a sodium alginate hydrogel layer

  • Datos identificativos

    Identificador: TFM:591
  • Autores:

    Tapusa, Ana Maria
  • Otros:

    Palabras clave: Membrana polimèrica, transport de protons, cel·la de metanol Polymeric membrane, proton transport, methanol fuel cell Membrana polimérica, transporte de protones, celdas de metanol
    Título en diferentes idiomas: Membrana biomimètica polimèrica per al transport de protons i canalitzada per autoensablatge columnar i intercalada amb un hidrogel d'alginat de sodi Biomimetic polymeric membrane for proton transport channeled by self-columnar assembly and sandwiched with a sodium alginate hydrogel layer Membrana biomimética polimérica para el transporte de protones y camalizada por autoensamblaje columnar e intercalada con un hidrogel de alginato de sodio
    Áreas temàticas: Química Chemistry Química
    Confidencialidad: No
    Curso académico: 2018-2019
    Estudiante: Tapusa, Ana Maria
    Departamento: Enginyeria Química
    Fecha de la defensa del trabajo: 2019-06-09
    Creditos del TFM: 24
    Director del proyecto: Giamberini, Marta
    Resumen: La poli (epicloridrina-co-oxid d’etilè) (PECH-co-EO), es va modificar amb unitats mesogèniques de 3,4,5-tris [4- (n-dodecan-1-iloxi) benzoiloxi] benzoat (grup TAPER) i es va caracteritzar per a la producció de membranes per al transport iònic. Es van aconseguir diferents graus de modificacions: 68% i 100% pel que fa a les unitats d’epicloridrina. Els monòmers implicats en la síntesi del grup TAPER i del polímer modificat amb aquest grup es van caracteritzar per ressonància magnètica nuclear de protó i de carboni (RMN). Aquest darrer producte també es va caracteritzar per una colorimetria diferencial d’escombrat (DSC) i amb microscòpia òptica polaritzada (POM). Finalment, es va sintetitzar material basat en alginat de sodi verge no reticulat i es van utilitzar diferents condicions per al seu entrecreuament. El FTIR va proporcionar el grau d’entrecreuament de membranes d'alginat de sodi i es van realitzar experiments de captació d'aigua. Poly (epichlorohydrin-co-ethylene oxide) (PECH-co-EO), was modified with mesogenic potassium 3,4,5-tris[4-(n-dodecan-1-yloxy) benzyloxy] benzoate (TAPER group) units and characterized for the production of membranes for ionic transport. Different degrees of modifications were achieved: 68% and 100% in regard to the epichlorohydrin units. The monomers involved in the TAPER’s group synthesis, the TAPER group and the obtained modified polymer were characterized by 1H and 13C nuclear magnetic resonance (NMR). This last one product was also characterized by differential scanning calorimetry (DSC) and polarized optical microscopy (POM). Finally, material based on un-crosslinked virgin sodium alginate was synthesized and different conditions were used for their crosslinking. The crosslinking degree of sodium alginate films was approach by FTIR and water uptake experiments were made. La poli (epicloridrina-co-óxido de etileno) (PECH-co-EO), se modificó con unidades mesogénicas de 3,4,5-tris [4- (n-Dodecaneso-1-iloxi) benzoiloxi] benzoato (grupo TAPER) y se caracterizó para la producción de membranas para el transporte iónico. Se lograron diferentes grados de modificaciones: 68% y 100% con respecto a las unidades de epicloridrina. Los monómeros implicados en la síntesis del grupo TAPER y el polímero modificado con este grupo se caracterizaron por resonancia magnética nuclear de protón y de carbono (RMN). Este último producto también se caracterizó por una colorimetría diferencial de barrido (DSC) y mediante microscopía óptica polarizada (POM). Finalmente, se sintetizó material basado en alginato de sodio virgen no reticulado y se utilizaron diferentes condiciones para su entrecruzamiento. El FTIR proporcionó el grado de entrecruzamiento de membranas de alginato de sodio y se realizaron experimentos de captación de agua.
    Materia: Química
    Entidad: Universitat Rovira i Virgili (URV)
    Idioma: Anglès
    Enseñanza(s): Enginyeria Química
    Título en la lengua original: Biomimetic polymeric membrane for proton transport channeled by self-columnar assembly and sandwiched with a sodium alginate hydrogel layer
    Fecha de alta en el repositorio: 2021-03-10
  • Palabras clave:

    Química
    Chemistry
    Química
    Química
  • Documentos:

  • Cerca a google

    Search to google scholar