Autor segons l'article: Xavier Montané; Krzysztof Artur Bogdanowicz; Gianmarco Colace; Jose Antonio Reina; Pierfrancesco Cerruti; Albena Lederer; Marta Giamberini
Departament: Química Analítica i Química Orgànica Enginyeria Química
Autor/s de la URV: MONTANÉ MONTANÉ, XAVIER; Krzysztof Artur Bogdanowicz; Gianmarco Colace; REINA LOZANO, JOSÉ ANTONIO; Pierfrancesco Cerruti; Albena Lederer; GIAMBERINI ., MARTA
Paraules clau: Chemical modification Columnar mesophase Membranes
Resum: Poly[2-(aziridin-1-yl)ethanol] (PAZE) is a suitable polyamine candidate which can be dendronised with 3,4,5-tris[4-(n-dodecan-1-yloxy)benzyloxy]benzoic acid (TAP) in order to obtain liquid crystalline columnar polyamines, as previously reported. However, the resulting copolymers evidenced a strong tendency to crystallise which leads to the detriment of columnar phase stability and the mechanical properties of the resulting polymeric membranes. In order to overcome this drawback, we successfully prepared LC columnar polyamines based on poly[2-(aziridin-1-yl)ethanol] modified with both TAP and benzoyl chloride at different extents. The presence of the dendron group induces self-assembling into a columnar structure, due to an exo-recognition of the side-chain dendrons, while the benzoyl group is expected to inhibit polymer crystallinity. All copolymers, except one, have lower melting points and exhibit higher clearing temperatures (Tc), when compared to the LC polyamines obtained by modification of PAZE with TAP only, reported in previous studies. In all cases they exhibited LC columnar mesophases after annealing, as inferred by DSC, XRD and POM. When casted as membranes, these columnar copolyamines can be homeotropically oriented under thermal treatment at optimal conditions, as was confirmed by X-ray diffraction studies at low 2θ angles. Additionally, SEM microscopy was used in order to evaluate the morphology of the prepared membranes.
Grup de recerca: Polimers Meteorgrup
Àrees temàtiques: Química Química Chemistry
Accès a la llicència d'ús: https://creativecommons.org/licenses/by/3.0/es/
ISSN: 0032-3861
Identificador de l'autor: 0000-0002-1426-239X; 0000-0001-8526-626X; n/a; 0000-0002-9245-4135; 0000-0003-0822-2866; n/a; 0000-0001-8278-3552
Data d'alta del registre: 2016-11-23
Pàgina final: 309
Volum de revista: 105
Versió de l'article dipositat: info:eu-repo/semantics/acceptedVersion
Enllaç font original: https://www.sciencedirect.com/science/article/abs/pii/S0032386116309661?via%3Dihub
URL Document de llicència: https://repositori.urv.cat/ca/proteccio-de-dades/
DOI de l'article: 10.1016/j.polymer.2016.10.047
Entitat: Universitat Rovira i Virgili
Any de publicació de la revista: 2016
Pàgina inicial: 298
Tipus de publicació: Article Artículo Article
Repositori URV