Resum: We report on the direct laser fabrication of step-index waveguides in fused silica substrates for operation in the 3.5 µm mid-infrared wavelength range. We demonstrate core-cladding index contrasts of 0.7%, enabling bends, low-loss coupling to commercial fluoride fibers, and propagation losses of 1.3 (6.5) dB/cm at 3.39 (3.68) µm, close to the intrinsic losses of the glass. We also report on the existence of three different laser modified SiO2 glass volumes, their different micro-Raman spectra, and their different temperature dependent populations of color centers, tentatively clarifying the SiO2 lattice changes which are related to the large index changes
Accès a la llicència d'ús: https://creativecommons.org/licenses/by/3.0/es/
ISSN: 0146-9592
Pàgina final: 5821
Volum de revista: 40
Versió de l'article dipositat: info:eu-repo/semantics/acceptedVersion
Enllaç font original: https://www.osapublishing.org/ol/abstract.cfm?uri=ol-40-24-5818
DOI de l'article: 10.1364/OL.40.005818
Entitat: Universitat Rovira i Virgili
Any de publicació de la revista: 2015
Pàgina inicial: 5818
Repositori URV