Autor segons l'article: Salagre, P.; Gebretsadik, F.B.; Llorca, J; Cesteros, Y.
Departament: Química Física i Inorgànica
Autor/s de la URV: SALAGRE CARNERO, MARÍA PILAR; Gebretsadik, F.B.; Llorca, J; CESTEROS FERNÁNDEZ, YOLANDA
Paraules clau: Copper nickel Hydrogenolysis
Resum: Ni and Cu mono- and bi-metallic catalysts modified with various types of acid oxides MOx (M = Mo, V, W and Re) were tested for hydrogenolysis of glycidol, as alternative route to hydrogenolysis of glycerol to obtain 1,3-propanediol. Characterization results revealed that the presence of modifiers affected dispersion and reducibility of the NiO particles, and the strength and amount of the acid sites. Among the modifiers tested, Re showed the highest activity, high propanediols selectivity and the highest 1,3-PrD/ 1,2-PrD ratio. Ni-Cu/Re ratio was optimized to improve the catalytic activity. The best catalytic result, with 46 % 1,3-PrD yield and 1,3-PrD/1,2-PrD ratio of 1.24, was obtained when monometallic Ni catalyst at 40 wt % loading and modified with 7 wt % Re was used at 393 K, 5 MPa H2 pressure after 4 h of reaction. The overall 1,3-PrD yield starting from glycerol and assuming a two-step synthesis (Glycerol Glycidol 1,3-PrD) and a yield of 78% for the first step, would be 36 %. This 1,3-PD yield is the highest for non-noble metal catalyzed reaction and is comparable to direct hydrogenolysis of glycerol using noble metal catalysts, at longer time and high H2 pressure.
Grup de recerca: Materials Catalítics en Química Verda
Àrees temàtiques: Química Química Chemistry
Accès a la llicència d'ús: https://creativecommons.org/licenses/by/3.0/es/
ISSN: 1867-3880
Identificador de l'autor: 0000-0003-3257-2022; ; ; 0000-0002-5439-9358
Data d'alta del registre: 2018-03-15
Pàgina final: 3680
Volum de revista: 9
Versió de l'article dipositat: info:eu-repo/semantics/acceptedVersion
Enllaç font original: http://onlinelibrary.wiley.com/doi/10.1002/cctc.201700536/abstract
Programa de finançament: CTQ2011-24610
URL Document de llicència: https://repositori.urv.cat/ca/proteccio-de-dades/
DOI de l'article: 10.1002/cctc.201700536
Entitat: Universitat Rovira i Virgili
Any de publicació de la revista: 2017
Pàgina inicial: 3670
Tipus de publicació: Article Artículo Article
Repositori URV