Passively Q-switched femtosecond-laser-written thulium waveguide laser based on evanescent field interaction with carbon nanotubes

Identificador:  imarina:4090811

Handle: https://hdl.handle.net/20.500.11797/imarina4090811

Autors:  Kifle, Esrom; Loiko, Pavel; Vazquez de Aldana, Javier Rodriguez; Romero, Carolina; Rodenas, Airan; Choi, Sun Yung; Bae, Ji Eun; Rotermund, Fabian; Zakharov, Viktor; Veniaminov, Andrey; Aguilo, Magdalena; Diaz, Francesc; Griebner, Uwe; Petrov, Valentin; Mateos, Xavier

Resum:
© 2018 Chinese Laser Press. Surface channel waveguides (WGs) were fabricated in a monoclinic Tm3:KLu WO4 2 crystal by femtosecond direct laser writing (fs-DLW). The WGs consisted of a half-ring cladding with diameters of 50 and 60 μm located just beneath the crystal surface. They were characterized by confocal laser microscopy and μ-Raman spectroscopy, indicating a reduced crystallinity and stress-induced birefringence of the WG cladding. In continuous-wave (CW) mode, under Ti:sapphire laser pumping at 802 nm, the maximum output power reached 171.1 mW at 1847.4 nm, corresponding to a slope efficiency η of 37.8% for the 60 μm diameter WG. The WG propagation loss was 0.7 0.3 dB∕cm. The top surface of the WGs was spin-coated by a polymethyl methacrylate film containing randomly oriented (spaghetti-like) arc-discharge single-walled carbon nanotubes serving as a saturable absorber based on evanescent field coupling. Stable passively Q-switched (PQS) operation was achieved. The PQS 60 μm diameter WG laser generated a record output power of 150 mW at 1846.8 nm with η 34.6%. The conversion efficiency with respect to the CW mode was 87.6%. The best pulse characteristics (energy/duration) were 105.6 nJ/98 ns at a repetition rate of 1.42 MHz.