Thermal Lensing and Multiwatt Microchip Laser Operation of Yb:YCOB Crystals

Identificador:  imarina:9242003

Handle: https://hdl.handle.net/20.500.11797/imarina9242003

Autors:  Loiko, Pavel; Maria Serres, Josep; Mateos, Xavier; Yu, Haohai; Zhang, Huaijin; Liu, Junhai; Yumashev, Konstantin; Griebner, Uwe; Petrov, Valentin; Aguilo, Magdalena; Diaz, Francesc

Resum:
Thermal lensing is studied in monoclinic Yb:Ca4YO(BO3)(3) (Yb:YCOB) oxoborate crystals cut along the optical indicatrix axes. For all orientations, the thermal lens is positive. In the Z-cut crystal, the sensitivity factors of the thermal lens are MZ-X = 2.4 and MZ-Y = 2.8 m(-1)/W (for E parallel to X), and the astigmatism degree is as low as S/M = 14%. The positive thermal lens in Yb:YCOB is related to the large thermal expansion and strong photoelastic effect. Microchip lasers are realized with 3-mm-long X, Y, and Z-cut 15 at.% Yb:YCOB crystals. With a Z-cut crystal, maximum output power of 8.35 W is achieved at similar to 1040 nm with slope efficiency of 70%. Using various crystal cuts and output coupler transmissions, multiwatt emission in the spectral range of 1033-1091 nm is demonstrated.