Growth

Identificador:  imarina:9294629

Handle: https://hdl.handle.net/20.500.11797/imarina9294629

Autors:  Subbotin, Kirill; Titov, Anatolii; Lis, Denis; Zimina, Yulia; Didenko, Yana; Elabedine, Ghassen Zin; Eremeev, Kirill; Sole, Rosa Maria; Aguilo, Magdalena; Volkov, Pavel; Popov, Pavel; Chernova, Elena; Diaz, Francesc; Camy, Patrice; Loiko, Pavel; Mateos, Xavier

Resum:
Thulium-doped magnesium molybdate single-crystal (Tm3+:MgMoO4) was grown by the Czochralski method (melting point: 1322 °C). The actual Tm3+ doping level was measured to be 0.1 at.% (the segregation coefficient was only 0.02). Tm:MgMoO4 belongs to the monoclinic class (sp. gr. C2/m, lattice constants: a = 10.2769(2) Å, b = 9.2898(5) Å, c = 7.0269(4) Å, β = 106.898(6)°). The thermal expansion tensor of this crystal is determined. Its thermal conductivity is also measured at 50–300 K (at room temperature, it amounts to 2.64 Wm−1K−1). Polarized Raman spectra are presented and the strongest mode is found at 957 cm−1. Optical spectroscopy of Tm3+ ions is studied indicating broad emission bands extending beyond 2 μm (the 3F4 → 3H6 transition) and a long lifetime of the 3F4 excited-state (1.972 ms). This makes Tm:MgMoO4 promising for broadly tunable and mode-locked lasers, when the technological problem of fabricating crystals with higher Tm3+ concentrations will be solved.