Spectroscopic and lasing characteristics of Yb:YGG at cryogenic temperatures

Identificador:  imarina:9322196

Handle: https://hdl.handle.net/20.500.11797/imarina9322196

Autors:  Slimi, Sami; Jambunathan, Venkatesan; Elabedine, Ghassen Zin; Yu, Haohai; Zhang, Huaijin; Chen, Weidong; Sole, Rosa Maria; Aguilo, Magdalena; Diaz, Francesc; Smrz, Martin; Mocek, Tomas; Mateos, Xavier

Resum:
We report on the optical spectroscopy and continuous-wave (CW) laser operation of ytterbium-doped yttrium gallium garnet (Yb:YGG) crystal at cryogenic temperatures. A maximum absorption cross-section of 1.7 × 10-20 cm2 with spectral bandwidth of 2.4 nm centered at 970.5 nm and a maximum emission cross-section of 6.5 × 10-20 cm2 with spectral bandwidth of 4.6 nm centered at 1024 nm were determined at 120 K. Cryogenic continuous-wave laser operation was achieved using a VBG stabilized laser diode emitting around 969 nm as pump source. At 120 K, a maximum output power of 17.50 W was achieved around 1024 nm corresponding to a slope efficiency of 87% with respect to the absorbed power.