Direct Writing of Quasi-Sinusoidal and Blazed Surface Relief Optical Transmission Gratings in Bi12GeO20, Er: LiNbO3 and Er: Fe: LiNbO3 Crystals by Nitrogen Ion Microbeams of 5 MeV and 10.5 MeV Energy

Identificador:  imarina:9446245

Handle: https://hdl.handle.net/20.500.11797/imarina9446245

Autors:  Bányász, I; Nagy, G; Havránek, V; Pujol, MC; Szokol, AN; Kármán, G; Magnusson, R; Rajta, I

Resum:
High diffraction efficiency optical transmission gratings with quasi-sinusoidal and saw-tooth surface relief profiles were fabricated in Bi12GeO20, Er: LiNbO3 and Er: Fe: LiNbO3 crystals by ion beam implantation. The gratings were directly written by nitrogen ion microbeams at energies of 5 MeV and 10.5 MeV. The finest grating constant was 4 mu m. Grating constants for the majority of the gratings were 16 mu m. The highest amplitudes of the gratings reached 1600 nm. The highest first-order diffraction efficiency obtained in a sinusoidal grating was 25%, close to the theoretical maximum of 33%. The highest first-order diffraction efficiency of a blazed grating was also 25%, without Littrow optimization. Such gratings can be incorporated into integrated optical biosensors.