Autor segons l'article: Mateos, X. ; Kurilchik, S. ; Loiko, P; Yasukevich, A. ; Trifonov, V. ; Volokitina, A. ; Vilejshikova, E. ; Kisel, V. ; Baranov, A. ; Goriev, O. ; Kuleshov, N. ; Pavlyuk, A.
Departament: Química Física i Inorgànica
Autor/s de la URV: MATEOS FERRÉ, XAVIER; Kurilchik, S. ; Loiko, P; Yasukevich, A. ; Trifonov, V. ; Volokitina, A. ; Vilejshikova, E. ; Kisel, V. ; Baranov, A. ; Goriev, O. ; Kuleshov, N. ; Pavlyuk, A.
Paraules clau: molybdate crystals Ytterbium lasers stimulated-emission
Resum: Crystal with composition Li2Zn2(MoO4)3 doped with 0.7 at.% Yb (Yb:LiZnMo), with high optical quality and few cm long is grown from the flux using Li2MoO4 as a solvent. Yb:LiZnMo is orthorombic (sp. gr. Pnma, a = 5.0843 Å, b = 10.4927 Å, c = 17.6742 Å, Z = 4). Polarized Raman spectra are studied for this crystal; the most intense band is observed at 898 cm-1. The ab-sorption, stimulated-emission and gain cross-sections of Yb3+ ions are deter-mined for the principal light polarizations, E || a, b, c. The maximum ¿SE = 6.6×10-21 cm2 at 1011 nm for E || b. The gain bandwidth for Yb:LiZnMo is up to ~50 nm. The radiative lifetime of the Yb3+ ions is 1.55 ms. The Yb:LiZnMo crystals are very promising for broadly tunable lasers.
Grup de recerca: Física i Cristal.lografia de Materials
Àrees temàtiques: Química Química Chemistry
Accès a la llicència d'ús: https://creativecommons.org/licenses/by/3.0/es/
ISSN: 1612-2011
Identificador de l'autor: 0000-0003-1940-1990; ; ; ; ; ; ; ; ; ; ;
Data d'alta del registre: 2018-07-25
Versió de l'article dipositat: info:eu-repo/semantics/submittedVersion
Enllaç font original: https://iopscience.iop.org/article/10.1088/1612-202X/aa7603/meta
URL Document de llicència: https://repositori.urv.cat/ca/proteccio-de-dades/
DOI de l'article: 10.1088/1612-202X/aa7603
Entitat: Universitat Rovira i Virgili
Any de publicació de la revista: 2017
Tipus de publicació: Article Artículo Article
Repositori URV