Palabras clave: molybdate crystals Ytterbium lasers stimulated-emission
Resumen: Crystal with composition Li2Zn2(MoO4)3 doped with 0.7 at.% Yb (Yb:LiZnMo), with high optical quality and few cm long is grown from the flux using Li2MoO4 as a solvent. Yb:LiZnMo is orthorombic (sp. gr. Pnma, a = 5.0843 Å, b = 10.4927 Å, c = 17.6742 Å, Z = 4). Polarized Raman spectra are studied for this crystal; the most intense band is observed at 898 cm-1. The ab-sorption, stimulated-emission and gain cross-sections of Yb3+ ions are deter-mined for the principal light polarizations, E || a, b, c. The maximum ¿SE = 6.6×10-21 cm2 at 1011 nm for E || b. The gain bandwidth for Yb:LiZnMo is up to ~50 nm. The radiative lifetime of the Yb3+ ions is 1.55 ms. The Yb:LiZnMo crystals are very promising for broadly tunable lasers.
Grupo de investigación: Física i Cristal.lografia de Materials
Áreas temáticas: Química Química Chemistry
Acceso a la licencia de uso: https://creativecommons.org/licenses/by/3.0/es/
ISSN: 1612-2011
Identificador del autor: 0000-0003-1940-1990; ; ; ; ; ; ; ; ; ; ;
Fecha de alta del registro: 2018-07-25
Versión del articulo depositado: info:eu-repo/semantics/submittedVersion
Enlace a la fuente original: https://iopscience.iop.org/article/10.1088/1612-202X/aa7603/meta
URL Documento de licencia: https://repositori.urv.cat/ca/proteccio-de-dades/
DOI del artículo: 10.1088/1612-202X/aa7603
Entidad: Universitat Rovira i Virgili
Año de publicación de la revista: 2017
Tipo de publicación: Article Artículo Article
Repositori URV