Disordered Tm:Ca9La(VO4)7: A novel crystal with potential for broadband tunable lasing

  • Datos identificativos

    Identificador: PC:2576
    Handle: https://hdl.handle.net/20.500.11797/PC2576
    Autores:
    X. MATEOSZ. ZHANGP. LOIKOH. WUJ. M. SERRESH. F. LINW. D. CHENG. ZHANGL. Z. ZHANGV. PETROVF. DÍAZM. AGUILÓU. GRIEBNERY. C. WANGE. VILEJSHIKOVAK. YUMASHEVZ. B. LIN
    Resumen:
    We report on the crystal growth, structural and spectroscopic investigation of a novel trigonal calcium vanadate crystal, Tm3+:Ca9La(VO4)7. Polarized absorption, stimulatedemission and gain cross-section spectra are determined for this material. The maximum ¿SE corresponding to the 3F4 ¿ 3H6 transition amounts to 1.28 × 10-20 cm2 at 1854 nm for ¿- polarization. The measured lifetime of the Tm3+ ions in the 3F4 state is 1.19 ms. The Judd- Ofelt analysis performed yielded intensity parameters of ¿2 = 4.682, ¿4 = 0.659 and ¿6 = 0.475 [10-20 cm2]. The polarized Raman spectra indicate a strong and broad band centered at 867 cm-1. Owing to the disordered nature of Ca9La(VO4)7, the Tm3+ ions exhibit a broad and smooth gain profile at ~2 ¿m. The spectroscopic properties of Tm3+:Ca9La(VO4)7 are very promising for broadly tunable and ultrashort pulse lasers near 2 ¿m.

  • Otros:

    Autor según el artículo: X. MATEOS; Z. ZHANG; P. LOIKO; H. WU; J. M. SERRES; H. F. LIN; W. D. CHEN; G. ZHANG; L. Z. ZHANG; V. PETROV; F. DÍAZ; M. AGUILÓ; U. GRIEBNER; Y. C. WANG; E. VILEJSHIKOVA; K. YUMASHEV; Z. B. LIN
    Departamento: Química Física i Inorgànica
    Autor/es de la URV: MATEOS FERRÉ, XAVIER; Z. ZHANG; P. LOIKO; H. WU; J. M. SERRES; H. F. LIN; W. D. CHEN; G. ZHANG; L. Z. ZHANG; V. PETROV; DÍAZ GONZÁLEZ, FRANCISCO MANUEL; AGUILÓ DÍAZ, MAGDALENA; U. GRIEBNER; Y. C. WANG; E. VILEJSHIKOVA; K. YUMASHEV; Z. B. LIN
    Palabras clave: Ultrashort pulses Tunable lasing Calcium
    Resumen: We report on the crystal growth, structural and spectroscopic investigation of a novel trigonal calcium vanadate crystal, Tm3+:Ca9La(VO4)7. Polarized absorption, stimulatedemission and gain cross-section spectra are determined for this material. The maximum ¿SE corresponding to the 3F4 ¿ 3H6 transition amounts to 1.28 × 10-20 cm2 at 1854 nm for ¿- polarization. The measured lifetime of the Tm3+ ions in the 3F4 state is 1.19 ms. The Judd- Ofelt analysis performed yielded intensity parameters of ¿2 = 4.682, ¿4 = 0.659 and ¿6 = 0.475 [10-20 cm2]. The polarized Raman spectra indicate a strong and broad band centered at 867 cm-1. Owing to the disordered nature of Ca9La(VO4)7, the Tm3+ ions exhibit a broad and smooth gain profile at ~2 ¿m. The spectroscopic properties of Tm3+:Ca9La(VO4)7 are very promising for broadly tunable and ultrashort pulse lasers near 2 ¿m.
    Grupo de investigación: Física i Cristal.lografia de Materials Física i Cristal·lografia de Nanomaterials
    Áreas temáticas: Química Química Chemistry
    Acceso a la licencia de uso: https://creativecommons.org/licenses/by/3.0/es/
    ISSN: 2159-3930
    Identificador del autor: 0000-0003-1940-1990; n/a; 0000-0002-4270-0668; n/a; 0000-0002-4299-538X; n/a; n/a; n/a; n/a; n/a; 0000-0003-4581-4967; 0000-0001-6130-9579; n/a; n/a; n/a; n/a; n/a
    Fecha de alta del registro: 2017-02-23
    Página final: 493
    Volumen de revista: 7
    Versión del articulo depositado: info:eu-repo/semantics/publishedVersion
    Enlace a la fuente original: https://www.osapublishing.org/ome/abstract.cfm?uri=ome-7-2-484
    URL Documento de licencia: https://repositori.urv.cat/ca/proteccio-de-dades/
    DOI del artículo: 10.1364/OME.7.000484
    Entidad: Universitat Rovira i Virgili
    Año de publicación de la revista: 2017
    Página inicial: 484
    Tipo de publicación: Article Artículo Article

  • Palabras clave:

    Calci
    Làsers sintonitzables
    Ultrashort pulses
    Tunable lasing
    Calcium
    Química
    Química
    Chemistry
    2159-3930

  • Documentos:

    DocumentPrincipal

  • Cerca a google

    Search to google scholar